TECHNICAL BULLETIN 02131 POLYISOCYANURATE VS. CELLULAR GLASS MECHANICAL INSULATIONPURP...
SUMMARY  K-factor: the aged thermal conductivity (k-factor) at 75°F of ISO-C1 polyiso is 0.176 Btu·in/hr·...
 WVT and Vapor Barriers: although cell glass manufacturers sometimes advertise that vapor barriers are not requi...
for very large pipe, multiple (more than two) cellular glass segments are required, resulting in more joints and ...
can shatter and lose its insulating integrity when severely thermally or mechanically shocked; when exposed to flame...
contractions/expansion joints the issue is mute since any temporary or permanent changes in dimension can be acco...
barrierClosed cell structure Yes YesFiber free Yes ...
of 7

Technical Bulletin 0213 Polyisocyanurate vs. Cellular Glass Insulation

This Technical Bulletin is another in our series of white papers aimed at providing our clients, engineers, specifiers, contractors, fabricators, and friends with objective information on our products and those of our competitors. This Bulletin focuses on a comparison of the physical properties of closed cell2 polyisocyanurate3 (polyiso or PIR) rigid foam insulation products with those of cellular glass insulation products for demanding below-ambient applications such as cryogenic, refrigerant, and chilled water where energy efficiency, moisture intrusion, and condensation are issues.
Published on: Mar 6, 2016
Published in: Technology      Business      Lifestyle      
Source: www.slideshare.net


Transcripts - Technical Bulletin 0213 Polyisocyanurate vs. Cellular Glass Insulation

  • 1. TECHNICAL BULLETIN 02131 POLYISOCYANURATE VS. CELLULAR GLASS MECHANICAL INSULATIONPURPOSEThis Technical Bulletin is another in our series of white papers aimed at providing our clients,engineers, specifiers, contractors, fabricators, and friends with objective information on ourproducts and those of our competitors. This Bulletin focuses on a comparison of the physicalproperties of closed cell2 polyisocyanurate3 (polyiso or PIR) rigid foam insulation products withthose of cellular glass insulation products for demanding below-ambient applications such ascryogenic, refrigerant, and chilled water where energy efficiency, moisture intrusion, andcondensation are issues.We strive to be objective and believe in full-disclosure. In that vein it should be said that cellularglass is a proven product made by reputable manufacturers, and it may be the most appropriateinsulant in some situations; for example in a chemically corrosive environments when 25/50flame spread/smoke development4 is required there is no better choice. Yet, as they say, the devilis in the details and insulation systems for low-temperature applications require engineeringexpertise that we do not purport to offer in this short Bulletin. Rather, we desire to raise issuesthat should be addressed by your engineer/specifier, and we will gladly provide any support orclarifying detail we may have.Simply, we offer that polyiso insulation products are the preferable choice for a range of lowtemperature applications, particularly cryogenic, refrigeration, HVAC, and even domestic hotand cold water applications ranging from minus 297°F up to plus 375°F service temperature.Specifiers, engineers, and end-users should additionally note that while this Bulletin is focusedon generic differences between cellular glass and PIR foams, yet there are indeed additionaldifferences between the physical properties and performance characteristics of competing PIRinsulations. We recommend end-users view other Technical Bulletins from Dyplast that addressISO-C1® and ISO-HT™ properties in comparison to alternative polyiso insulation products.1 Update on Technical Bulletin 06102 Determination of “closed celled” versus “open celled” is not as simple as it would first seem, since thereare variations in the “%” of closed cells, as well as variation in cell structure and whether they can retaininsulating gases. We could not find a statement from cell glass manufacturers re: % closed cells, but it is 3logical that it is very high. ISO-C1 has >95% closed cells in its 2 lb/ft density, and >98% in higher density.3 Polyisocyanurate is a form of polyurethane (PUR), but the chemistry and properties are different.4 No U.S. manufactured polyiso currently meets the 25/50 criteria; however Dyplast’s ISO-C1 and ISO-HTmeet Class 1 per ASTM E84.Technical Bulletin 0213 Page 1 of 7 February 2013
  • 2. SUMMARY  K-factor: the aged thermal conductivity (k-factor) at 75°F of ISO-C1 polyiso is 0.176 Btu·in/hr·ft2·°F whereas FoamGlas brand cellular glass is 0.29; thus the thermal insulation performance of cellular glass is roughly 65% worse than polyiso, which results in cellular glass insulation systems being much thicker (important from a weight, volume, quantity of accessory products such as sealants, jackets, etc., and space aspects).  Brittleness and Shipment/Handling: cellular glass is more susceptible than polyiso to vibration, thermal shock, and mechanical shock; thus cellular glass may have breakage during transportation to the job site and subsequent handling; polyiso is not of course immune to damage during shipment or handling but typically requires less mitigation efforts; thumbrules for cellular glass from insulation specifiers and contractors sometimes assume 5% breakage during shipment, 15% breakage from handling on job site.  Brittleness and Operations: cellular glass may be less suitable for application in process environments with high vibration, movement, or thermal/mechanical shock; cellular glass breaks or cracks may create a path for heat and/or moisture to pass; polyiso is not brittle and is not as susceptible to vibration, movement, or thermal/mechanical shock; when polyiso is installed in areas where mechanical abuse is expected, such as workers stepping on the insulation, higher density polyiso with higher compressive strengths should be considered; even when abused, since polyiso is not brittle so it will not crack like cellular glass so such thermal/moisture leaks are less likely to form.  Thermal Expansion/Contraction: since cellular glass has a thermal expansion coefficient less than polyiso, expansion joints are less of an issue; pipe metallurgy and the range/duration of temperature cycling are determining factors yet our experience is that the cost of additional expansion joints is not material when insulant selections are being made.  Water Vapor Transmission and Joints/Cracks: (i.e. WVT, or permeability): both polyiso and cellular glass are “low perm” materials; cellular glass manufacturers generally advertise “zero” perm; polyiso insulation has low (but not zero5) water vapor permeability; for both materials we contend that the risk of moisture infiltration is less determined by the inherent property of polyiso or cell glass and more-so dependent on the number of joints between insulant segments6, the quality/performance of joint sealants, and the likelihood of cracks in the insulation; both cellular glass and polyiso manufacturers recommend vapor retarders in cold service.5 ISO-C1 polyiso has 1.65 perm-inch WVT; Trymer polyiso advertises 4.06 Polyiso is manufactured as large continuous “bunstock” that can be fabricated into pipe insulation manytimes larger than is possible with cell glass, thus minimizing the number of joints and seams; ask yoursupplier for specific dimensionsTechnical Bulletin 0213 Page 2 of 7 February 2013
  • 3.  WVT and Vapor Barriers: although cell glass manufacturers sometimes advertise that vapor barriers are not required, polyiso manufacturers more often recognize that in low temperature applications engineers almost always specify that a vapor barrier be applied over the insulant - - not so much to improve the WVT of the insulant but as a second line of defense for the joints, seams, and cracks; thus given the facts in the prior paragraph, vapor barriers are arguably more important in cell glass systems than polyiso systems.  Water Absorption (WA): Although different ASTM standards govern the testing of WA in polyiso and cellular glass7, each have excellent water absorption properties, and water absorption should not be a factor in a properly installed insulation system.  Installation – the “insulation system”: A particular insulation product can perform at its peak only when properly installed within a more complete “insulation system” with sealants, adhesives, vapor barriers, weather mastics, jacketing, and so forth; while some cellular glass manufacturers advertise that neither vapor barriers nor jackets are required, the fact is that the vast majority of engineer/specifiers require similar accessory components; in fact, cellular glass insulation systems may require more complexities than a comparable polyiso insulation system, and thus may be more time-consuming to install and thus may have more potential for errors during the installation process; for example, a cellular glass system for LNG pipe may require an abrasive-resistant coating, a latex mastic as a weather barrier mastic (3 - 4 gal./100 ft2 ), then a layer of synthetic mesh fabric, and then a second coat of weather barrier coating, and possibly a metal jacket’ whereas a polyiso system installation would require only a sealant on seams/joints/ butt- ends, and a vapor barrier sheeting over the insulation (and this could actually be shop applied, making field installation even easier) and protective metal jacketing; note of course that polyiso systems as well as cellular glass systems require mastics at vapor stops and potentially other discontinuities; thumbrules from insulation contractors indicate that cellular glass requires a minimum of 30% more labor to apply than polyiso.  Installation – field fabrication: installation contractors may have varied opinions on whether cellular glass or polyiso is easier to field fabricate (change shape/dimensions at the jobsite); cellular glass can be shaped by abrading it against a rough surface (or even the pipe itself, although maybe not advisable) or by using a rasp; some installers have minor complaints relating to abrasion to a worker’s hands, glass dust, and odor; and the density/weight of cellular makes it somewhat more difficult for workers to handle; on the other hand, polyiso is shaped or re-shaped in the field typically with a sharp knife also it can also be shaped with a rasp; the most common complaint from installers is dust.  Installation – number of insulation segments: the maximum dimensions of cellular glass insulation blocks are less than those of polyiso bunstock, and therefore when larger pipe diameters are involved, the cellular glass blocks must be joined together with adhesives;7 The percent by volume WA for ISO-C1 polyiso is 0.04%, and for Trymer <0.7%; and for cellular glass<0.2%Technical Bulletin 0213 Page 3 of 7 February 2013
  • 4. for very large pipe, multiple (more than two) cellular glass segments are required, resulting in more joints and seams to seal, which means more labor, more consumption of materials, and more possibility of improper installation (e.g. a seam not sealed, or a cracked piece of insulation) - - which can lead to thermal and/or moisture leaks; polyiso bunstock on the other hand is large enough to be fabricated into two half-shells even for the largest of pipe diameters; due to cellular glass’s poorer insulating properties, a cellular glass insulation system is also likely to have more layers than a comparable polyiso system thus requiring more steps in the process, more joints to seal, and resulting in more consumption of sealants, tapes, adhesives, etc.  Number of Layers: Some cellular glass manufacturers state that fewer layers of insulation are required with cell glass; since cell glass is typically manufactured in smaller dimensions that must be glued together and that each segment has materially lower R- values we would suggest that this be challenged; for instance, the cell glass equivalent of a 4 inch thick layer of polyiso at a 0.176 k-factor would require almost 7 inches of cellular glass; multiple layers of insulant are generally specified not to add more thermal efficiency8 but rather to allow offsetting joints and seams - - thus mitigating risks of moisture infiltrations.  Weight: Cellular glass has a density of generally 7.5 lb/ft3 versus 2.0 lb/ft3 for the most commonly used polyiso9; the low thermal efficiency of cellular glass (65% worse than polyiso) compounds the problem since cellular glass installations may require closer to double the thickness to provide the same insulating performance; the result is a significant increase in weight and volume on a given pipe run [for example assume an 8 inch diameter run of piping requiring 2 inch of polyiso insulation at 2 lb/ft3 density; every linear foot of insulation would weigh 0.87 lbs; since 3.5 inch thick10 cellular glass must be applied to achieve the same R-value, a linear foot of cell glass would be 6.6 lbs - - 7.5 times more weight than polyiso]; the costs of additional pipe hangars, stress on joints that can lead to failure, and inability to run multiple pipes in a small space may make cellular glass a less suitable insulation.  Combustibility: Cellular glass has a zero flame spread index (FSI) and a zero smoke developed index (SDI) per ASTM E84; polyiso insulation products for mechanical insulation made in the U.S. currently meet only Class 1, and cannot be installed when air plenum conditions are required; caution must be exercised when installing any insulant in air plenum environments since vapor retarders, weather barriers, sealants, mesh, or adhesives may have non-compliant FSI/SDI characteristics; note also that cellular glass8 Two 3 inch layers of polyiso have the same thermal resistivity as a single 6 inch layer, yet two layersallow staggered joints & seams to provide another line of defense against moisture intrusion.9 3 For some LNG applications, density of polyiso may be 2.5-3 lb/ft .10 Using 3E-Plus software developed by North American Insulation Manufacturers Association, roundedto nearest ½ inch thickness.Technical Bulletin 0213 Page 4 of 7 February 2013
  • 5. can shatter and lose its insulating integrity when severely thermally or mechanically shocked; when exposed to flame, polyiso insulation will char, but maintain its shape, providing precious minutes of thermal protection to pipe, equipment, and vessels to allow response. [Important Note: Section 602.2.1 of the International Mechanical Code states that materials within return air plenums shall be either non-combustible or have less than or equal to a 25/50 fire spread index and developed smoke index when tested in accordance with ASTM E84. Interpretations by other code authorities allow compliance with NFPA 255 or UL 723 as substitutes for ASTM E84. Essentially this means that insulation systems (and all accessory components within, such as sealants, vapor barriers, etc.) installed in either air plenums or inhabited areas to be non-combustible or ≤ 25/50. Name-brand cellular glass such as FoamGlas meets this ≤25/50 requirement. ISO-C1 polyiso is 25/130, so it should not be installed in air plenums or in indoor inhabited areas. Caution should be observed when using cellular glass in such applications that all related sealants, barriers, and such are ≤ 25/50.]  Cost: The cost of cellular glass per linear foot generally exceeds that of polyiso by a material margin; the installation cost of cellular glass can be 2 to 3 times as expensive as polyiso; life-cycle costs relating to energy loss and maintenance also will favor polyiso over cellular glass.  Chemical resistance: Cellular glass is arguably impervious to the majority of chemicals and is indeed resistant to organic solvents and nearly all acids; yet in the vast majority of cryogenic, refrigerant, and chilled water applications such chemical resistance is not required; it is appropriate to caution that a chemical resistance concern must include accessory products such as sealants, mastics, and vapor retarders.  Compressive Strength: Cellular glass, at 7.5 lb/ft3 density indeed has high compressive strength up to typically 90 lb/in2, yet it should be noted that the compressive strength of 6 lb/ft3 density ISO-C1 is typically greater than 135 lb/in2 (parallel to rise); higher compressive strengths are most commonly required only in pipe saddle applications and in areas of high mechanical abuse, and in these applications polyiso insulation can offer high strength while enabling higher thermal efficiencies than cell glass - - and with fewer problems associated with cracking and weight management.  Coefficient of Linear Thermal Expansion (CLTE): Cellular glass has a CLTE close to that of metal, and thus requires fewer contraction/expansion joints than a polyiso insulation system; polyiso, however, is much easier to work in the field and polyiso contraction/expansion joints are relatively easy to install.  Dimensional Stability: Dimensional stability is a combination of both reversible and irreversible changes in linear and volumetric units; cellular glass product data sheets typically advertise excellent to extraordinary dimensional stability, yet polyiso insulants have very good to excellent characteristics; the bottom line is that with properly installedTechnical Bulletin 0213 Page 5 of 7 February 2013
  • 6. contractions/expansion joints the issue is mute since any temporary or permanent changes in dimension can be accommodated by insulation system design; note that some cellular glass manufacturers make comparisons against polyurethane insulation without noting that polyisocyanurate is a different chemical formulation with much improved dimensional stability; note also that ISO-C1 has the best dimensional stability when compared with competitive polyiso products.  Independent Testing and Auditing of Physical Properties: Although physical properties of insulants reported by manufacturers are generally credible, it is always prudent to expect validation of results by an independent third-party laboratory; even better, expect that the manufacturing and quality control protocols be periodically audited by an accredited agency.The following table displays key physical properties of polyiso (ISO-C1) and cellular glass(FoamGlas). Note that these are “product” values, and not “insulation system” values. Insulation Material Units Polyiso FoamGlas 2 Aged k-factor (at 75°F) Btu·in/hr·ft ·°F 0.176 0.29 WVT Perm-in 1.65 <0.01 Flammability ASTM E84 FSI/SDI 25/130 <25/50 rating (insulation only) per FM Density lb/ft3 2.0 7.5 Water Absorption11 % by volume <0.04 <0.2Qualitative Comparison Chart:Quality Polyiso Cellular GlassThermal Performance Excellent FairWVT without vapor barriers Very good ExcellentWVT with vapor barriers Excellent ExcellentASTM E84 FSI/SDI Very Good (Class 1) Excellent (< 25/50; sometimes advertised as 0/0)Available with factory-applied vapor Yes Yes11 Measured by different ASTM standards; cellular glass manufacturers frequently note that the water isretained on the surface only.Technical Bulletin 0213 Page 6 of 7 February 2013
  • 7. barrierClosed cell structure Yes YesFiber free Yes YesNon-porous Yes YesMold resistant Yes YesResistant to vibration/movement Yes Less soRequires a metal jacket Generally GenerallyThicknesses available Virtually unlimited, Limited, 1” minimum from 1/8” upwardsLengths Virtually any Sold in 3 foot maximumIn-field fabrication Easy Less easyTechnical Bulletin 0213 Page 7 of 7 February 2013